Stickler Coverall RP1001
All statements, technical information and recommendation are based on tests believed to be reliable, the accuracy or completeness thereof is not guaranteed, and the following is made in lieu of all warranties of merchantability and fitness for the purpose: Sellers and manufacturer’s only obligation shall be to replace such quantity of the product proved to be defective. Before using, user shall determine the suitability of the product for its intended use, and user assumes all risk and liability whatsoever in connection herewith.
NOTE: The substrate should be free of dust and lubricant before apply. Please use once unwrapped, if stock is to be returned to the storage shelf please ensure stock is wrapped and bagged to prevent surface dust and contamination. This product should be tested thoroughly under use condition to ensure it meets the requirements of the specific application.
Face Material:
|
Properties |
Test Method |
Result |
|
Grammage |
ISO 536 |
90 ± 5 g/m2 |
|
Caliper |
ISO 534 |
72 ± 5 microns |
Adhesive:
RP1001-Type Extra Permanent (Hot Melt)
A rubber based hot-melt adhesive with high tack and adhesion, particularly on difficult and apolar substrates (PE,PP). Improved recipe for high speed converting.
|
Properties |
Result |
|
Composition |
Rubber based Hot-Melt |
|
Minimum Application Temperature |
0ºC |
|
Service Temperature |
-10 to +70 ºC |
|
Food contact |
dry and moist direct |
|
Tack FTM9 N/inch² |
16 |
|
Ultimate adhesion FTM² N/inch |
9 |
Laminate:
Laminate Shelf Life 24 months stored at 23ºC/50% RH
Typical Laminate Calliper 151 microns / 173gsm
WG White glassine
WG white glassine backing allows high speed conversion and consistent dispensing on a wide range of equipment.
|
Properties |
Result |
|
Grammage |
63 gsm |
|
Opacity |
> 45% |
|
Caliper |
56 microns |