LG LC5521 & LG LC5522

LG LC5521 is a matt polymeric vinyl with a clear permanent adhesive and double sided PE coated paper liner that is perfect for short term indoor & outdoor window decoration applications.

Available in a matt white & matt black etch.

    • Perfect for short term indoor & outdoor window decoration applications
    • U pto 3 years vertical durability

    Physical Properties (LC5520, 5521, 5522, 5540, 5550M)

     Property

    Specification

    Test Method

    Thickness (Including adhesive)

    160㎛ ± 10%

    Micrometer

    Tensile strength

    ≥ 1.8kg/cm

    ASTM 882

    Elongation

    ≥ 100%

    ASTM 882

    Peel adhesion(24hrs)

    ≥ 800g/in

    180 peeling PSTC-1

    Service temp. range

    -25℃ ~ 82℃

    Film applied Al panels 24hrs prior test

    Application temp

    ≥ 10℃

    18 to 25℃ optimum, on clean substrate

    Opacity

    Tt >70

    Haze Meter (Tt: Transmission)

    Release liner thickness/weight

    0.14mm ± 10%/130g/sqm

    Micrometer

    Characteristics

    Item

    LC5510,5511,5560M

    LC5520,5521,5522,5540,5550M

    Film

    3.6 mils(0.09mm)

    5.1 mils(0.13mm)

    Thickness

    4.6 mils(0.115mm) with adhesive (± 10%)

    6.3 mils(0.16mm)with adhesive (± 10%)

    Adhesive

    Acrylic based pressure sensitive

    Adhesive color

    Clear

    Liner

    Clays coated paper(130g/㎡)

    Double sides PE coated paper(130g/㎡)

    Application surfaces

    Flat Surface

    Application temp.

    ≥ 10℃(18 to 25℃ optimum)

    All statements, technical information and recommendation are based on tests we believe to be reliable, but the accuracy or completeness thereof is not guaranteed, and the following is made in lieu of all warranties of merchantability and fitness for the purpose: Sellers and manufacturer’s only obligation shall be to replace such quantity of the product proved to be defective. Before using, user shall determine the suitability of the product for its intended use, and user assumes all risk and liability whatsoever in connection therewith.